Fiberglass woven roving is made directly of roving in plain or twill weave fabric.
Well-balanced thickness and expansion force with good vertical appearance.
Fast and balanced wet-out, good fittability, easily removing air bladder.
High mechanical strength, less strength loss in wet condition.
Because of its high mechanical property and corrosion resistance ability, the fabric is widely used in yacht, automobiles, sports equipment, cooling tower and etc.
Applicable process：Hand lay-up, RTM, Vacuum.
Compatible resin：Unsaturated polyester resin, Vinyl ester resin, Epoxy resin.
|Product Code||Unit weight||
Tensile Breaking Force
|EW100(T)||（100±8%）g/m2||Plain/(Twill)||≤2030 mm||0.10 mm|
|EW160(T)||（160±8%）g/m2||Plain/(Twill)||≤2030 mm||0.15 mm|
|EWR200(T)||（200±8%）g/m2||≥1300||≥1100||Plain/(Twill)||≤2000 mm||0.20 mm|
|EWR300(T)||（300±8%）g/m2||≥1900||≥1700||Plain/(Twill)||≤2000 mm||0.30 mm|
|EWR400(T)||（400±8%）g/m2||≥2500||≥2200||Plain/(Twill)||≤2000 mm||0.40 mm|
|EWR600 (T)||（600±8%）g/m2||≥4000||≥3850||Plain/(Twill)||≤2000 mm||0.60 mm|
|EWR800(T)||（800±8%）g/m2||≥4600||≥4400||Plain/(Twill)||≤3000 mm||0.80 mm|
* Special specifications can be produced according to customer requirements.
* All of the above models with T can be produced into twill.